if you try to anodize anything that is not aluminum it will most likely melt, i can confirm and by reading this thread, any steel stainless or mild which ever kind/quality, will melt and dissolve in the bath that is used to anodize/plate the metal, so really either do a metal plate not anodize, or just find a way to paint it, its not that it won't look cool, its just you lose your pieces and money
(i know this from working in a factory that does anodization, we put steel screws in to test it, there was nothing left not even in the bottom of the bath)
|